Resistive switching and battery
HomeHome > Blog > Resistive switching and battery

Resistive switching and battery

Aug 28, 2023

Scientific Reports volume 13, Article number: 14297 (2023) Cite this article

Metrics details

Highly transparent resistive-switching (RS) devices were fabricated by growing amorphous tantalum pentoxide (a-Ta2O5) and indium tin oxide (a-ITO) thin films on barium-borosilicate glass (7059) substrates, using electron beam evaporation. These layers exhibited the transmittance greater than ~ 85% in the full visible region and showed RS behavior and battery-like IV characteristics. The overall characteristics of RS can be tuned using the top electrode and the thickness of a-Ta2O5. Thinner films showed a conventional RS behavior, while thicker films with metal electrodes showed a battery-like characteristic, which could be explained by additional redox reactions and non-Faradaic capacitive effects. Devices having battery-like IV characteristics showed higher enhanced, retention and low-operation current.

Transparent resistive-switching (RS) devices have attracted significant scientific attention for developing invisible circuits, ultra-low power electronic devices, sensors, and transparent electronics1,2,3,4,5,6,7,8,9,10. Current research on transparent-conducting-oxides (TCO) requires a delicate balance between high electrical conductivity and optical transparency in the visible spectrum. Moreover, there is a need of embedding other circuitry elements on TCO that can perform other information processing and storage functionalities. Especially, the two-terminal RS device is promising to overcome the fundamental limitations of circuit complexity, scaling and power consumption8,11,12,13,14,15. In a typical RS device, the resistance is changed between low and high resistive states in a reversible and non-volatile manner under the application of electric fields and currents. Furthermore, the multilevel RS can also have intermediate-resistive-states (IRS) that can be stabilized in a single device using voltage, compliance-current and temperature, which could play a pivotal role for high-density storage16,17,18,19,20,21,22. Another related behavior is memristive type, where the resistance value is continuously modified with the history of applied voltage and current that can mimic the condition in the brain, in which the electrical connections between two neurons become stronger every time the connection is addressed21,23,24,25,26,27. Both memristive and multilevel switching characteristics are essential for the development of neuromorphic computing. Indeed, the same two-terminal RS devices (in capacitator geometry) can also be leveraged to provide the power locally, also called nanobatteries28,29 for increasing the portability and efficiency. High dielectric metal-oxides such as hafnium-oxide (a-HfOx), tantalum-oxide (a-TaxOy) and yttrium oxide (a-Y2O3) could be very promising materials for developing transparent-resistive-random-access-memory (T-RRAM) and memristive devices, that can be grown at low temperature22,30,31,32,33,34,35,36. Tantalum-oxides (a-Ta2O5) grown by various physical vapor deposition methods are highly promising as highly insulating transparent films can be grown at lower temperatures. Therefore, it would be interesting to elucidate the role of film thickness, electrode material, Joule’s heating, and whether or not transparent conducting oxide like indium tin oxide (ITO) can be effective integrated with tantalum-oxide for T-RRAM or transparent memristors. Here, we have found that some intermediate thickness regime showed a new kind of battery-like IV characteristics with enhanced endurance, retention and extremely low leakage current that is important for the low-power devices. We propose a non-Faradaic capacitive (NFC) effect could be responsible for this behavior. The opposing internal field helps in restricting the leakage current and improve the operation power in these devices. This study opens the opportunities of incorporating the concepts of nanobatteries in Ta2O5 based memristors and RS devices, and pose further questions related to the underlaying mechanisms of NFC.

Figure 1a illustrates the schematic diagram of resistive switching (RS) devices. To fabricate these devices, a highly transparent bottom electrode layer of amorphous Indium Tin Oxide (a-ITO) was first deposited on barium-borosilicate glass (Corning 7059 glass) using electron beam evaporation (EBE). After masking a region for the bottom contact, fresh layers of a-ITO of ~ 15 nm thickness and a-Ta2O5 of distinct thicknesses (~ 20 nm, ~ 40 nm, ~ 80 nm, ~ 130 nm, ~ 180 nm, ~ 270 nm) were deposited without breaking the vacuum to ensure a fresh interface. The EBE of a-ITO and a-Ta2O5 were performed using 99.999% pure granules of these materials under the oxygen partial pressure of ~ 2 × 10–5 Torr at substrate temperature ~ 200 °C and electron beam current of ~ 40 mA. The shadow mask was used to fabricate top metal electrodes where area of circular metal electrodes was found to be ~ 100 μm2. The thickness and roughness of these thin films were confirmed using the stylus profilometer and ellipsometry.

(a) schematic diagram of the resistive switching devices, (b) UV–Vis. Transmission vs Wavelength of individual layers, (c) Tauc plots to extract the bandgaps of individual layers, (d) The logarithmic variation of the absorption coefficient versus photon energy for ITO (~ 15 nm), TaxOy (~ 20 nm, ~ 80 nm), (e–f) The spectra of ellipsometric parameters, Δ (a) and ψ (b) verses wavelength (λ), (g,h) Real part (εr) and Imaginary part (εi) of the dielectric constant versus wavelength (λ).

UV–visible spectroscopy and ellipsometry are used to investigate the optical properties of these films. Figure 1b shows the transmittance spectra measured over the wavelength range of 250–800 nm of a-ITO and a-Ta2O5 of different thicknesses. The transmission of individual layers of a-Ta2O5 oxide and a-ITO is more than ~ 85% in the full visible region, and ~ 94% @ 550 nm wavelength. The Fabry–Perot oscillations in the UV–visible spectra are seen with increasing the film thicknesses, indicating high quality of these films and confirm the layer-by-layer smooth growth. The absorption coefficient of the film can be derived from the equation , where T, R and d are transmittance, reflectance, and thickness respective. It can be further simplified as for negligible reflectance. The bandgaps of these films were extracted from UV–Visible spectra using the Tauc plots, as shown in Fig. 1c, using the equation where \(h, v\) and \({E}_{g}\) are Plank’s constant, light frequency and bandgap respectively. The optical bandgap value of a-ITO is ~ 3.6 eV and a-Ta2O5 is ~ 4.5–4.8 eV, which is consistent with the literature values37,38 within the limitations of extracting bandgap using Tauc plots. The a-Ta2O5 films are highly insulating and transparent that indicate the very low oxygen vacancies and defects. To further understand the defects, the Urbach energy (Eu) can be extracted from the UV–Vis spectroscopy that indicate the band-tailing39 in amorphous this film due to the presence of disorders39. It can be derived from the exponential broadening of the absorption edge using the relation \(\alpha ={\alpha }_{0}\mathrm{exp}\frac{hv}{{E}_{u}}\). Figure 1d illustrates ln (α) vs hν plots and the corresponding slopes are mentioned on the corresponding curves. The inverse of the slope gives the approximate values of Eu for ITO ~ 200 meV and Ta2O5 ~ 115 meV (for ~ 20 nm), 131 meV (for ~ 40 nm) and ~ 161 meV (for ~ 80 nm). The increase in the Urbach energy with thickness indicate the formation of higher oxygen vacancies as the films are grown thicker. This is also consistent with the slight decrease in the overall transmission of these films as the thickness increases.

The optical and dielectric properties of these films were further investigated using the variable angle spectroscopic ellipsometer (VASE) model developed by J. A. Woollam, Inc. The ellipsometry measurements were carried out at an incident angle of 70° (close to Brewster's angle for these samples) at the wavelengths (λ) ranging from 250 to 1650 nm with energy resolution of ~ 0.01 eV. These results are shown in Fig. 1e–h. Here, the change in the polarization (ρ) of incident light is measured after the reflection from the sample surface which can be expressed as \(\rho = {r}_{p}/{r}_{s}\) , where \({r}_{s}\) and \({r}_{p}\) are the amplitude of s- and p- components reflected waves having oscillations parallel and perpendicular to the sample surface, respectively40. In a typical measurement, the complex reflectance ratio \(\rho =\frac{{r}_{p}}{{r}_{s}}=\mathrm{tan}(\psi ).\mathrm{exp }(i\Delta )\), where \(\mathrm{tan}(\psi )\) is amplitudes ratio and \(\Delta\) is the phase difference i.e \(\rho = \frac{\left|{r}_{p}\right|\mathrm{exp}(i{\delta }_{p})}{\left|{r}_{s}\right|\mathrm{exp}(i{\delta }_{s})}\). The parameters (\(\psi , \Delta )\) can be calculated using Fresnel equations using the iterative model. Here, we have used a two-layer optical model suitable for tantalum oxide thin films40, and the fitted graphs are shown in Fig. 1e,f. It is possible to see that the modelled fit spectra and experimental spectra coincide almost perfectly. These results indicate that \(\Delta\) is more sensitive to variations in film thickness than \(\psi\) throughout the range of thicknesses. Specifically, the thicker film and the thinner film showed little variation in the \(\psi\) vs. wavelength curves, although the equivalent curves for \(\Delta\) showed a huge variation. The film deposition parameters would have an impact on the "\(\psi , \Delta\)" values. Various optical parameters such as refractive index (n), extinction coefficient (k), film thickness, and roughness can be extracted as fitting parameters from Fig. 1e,f, as shown in the Supplementary Fig. S1c,d. The values of n and k are used to estimate the real and imaginary components of dielectric constants using the relation \({\varepsilon }_{r}={n}^{2}-{k}^{2}\) and \({\varepsilon }_{i}=2nk\) respectively, as shown in Fig. 1g,h as a function of wavelength. The imaginary part of the dielectric material corresponds to the dissipation or loss of incident photon energy inside the material. The refractive index (n) represents the part of the light that gets transmitted through the material without getting absorbed and depends on the chemical composition of the material. The extinction coefficient (k) depends on the defects present in the material. For a good dielectric material, imaginary part (or dissipation) should be as small as possible and real part should be large. Apparently, the large change in parameters (\(\psi , \Delta )\) and the dielectric constants (\({\varepsilon }_{r}, {\varepsilon }_{i})\) could be seen near the wavelengths (250–500 nm) near bandgap due to the band-to-band transitions40.

The accuracy of the fitting40,41 can be quantified as the root mean squared error \(MSE= \sqrt{\frac{1}{3m-1}}\sum_{i=1}^{m}\left[{\left({P}_{Ei}-{P}_{Gi}\right)}^{2}+{\left({D}_{Ei}-{D}_{Gi}\right)}^{2}+{{K}_{Ei}-{K}_{Gi})}^{2}\right]\times 1000\), where \(P=\mathrm{cos}\left(2\psi \right)\); \(D=\mathrm{sin}\left(2\psi \right)\mathrm{cos}\left(\delta \right)\); \(K=\mathrm{sin}\left(2\psi \right)\mathrm{sin}\left(\delta \right)\); m is the number of measured wavelengths and i is the iteration number. MSE values are found to be ~ 1 for all the thin films.

X-ray photoelectron spectroscopy (XPS) measurements were performed using a hemispherical electron energy analyzer with 20–50 eV pass energy with an energy resolution of ~ 1 eV at a base pressure of ~ 2 × 10−10 mbar. A non-monochromatic Al_Kα laboratory X-ray source was operated at ~ 196 W (14 mA and 14 kV). The specimens were mounted using a conducting carbon tape on a specially designed sample station42. The XPS data was analyzed with xpspeak41 software. The multiple peaks in XPS spectra were fitted using Gaussian function after Tougaard type background subtraction. The position of sp3 carbon 1 s peak is taken as a standard (binding energy 284.6 eV) to compensate for any charge-induced shifts. The spin- orbit splitting for Indium (In) and Tin (Sn) are 7.54 eV and 8.47 eV, respectively. The XPS spectra of a-ITO layer shows peaks around ~ 451.79 eV and ~ 454.12 eV related In 3d3/2 orbitals and ~ 446.49 eV and ~ 444.24 eV related to In 3d5/2 orbitals, as shown in Fig. 2a. On the other hand, Sn peaks 3d3/2 appears around ~ 496.96 eV and ~ 494.70 eV and Sn 3d5/2 peaks around ~ 488.40, ~ 486.18, as shown in Fig. 2b. The peaks ~ 442.09 eV and ~ 484.89 eV are satellite peak due to non-monochromatic x-ray source. The binding energy of In and Sn peaks indicate the valency of these elements are 3+ and 4+ respectively, that confirms the mixture of In2O3 and SnO2. Oxygen (O) 1 s orbital peak coincides well with ~ 529.7, ~ 531.8, ~ 534.0 with expected binding energy of In2O3 and SnO2 as shown in Fig. 2c. Similar results were observed in the literature paper43,44. The peak of In 3d5/2 at ~ 446.49 and O 1 s at ~ 534.0 peak may be attributed due to free hydroxyl groups which is possibly due to environmental moisture trapped in the film surface. XPS spectra of freshly grown a-Ta2O5 layer ~ 17 nm shows two sharp peaks at ~ 26.0 eV and ~ 27.9 eV in Fig. 2d related to tantalum (Ta) 4f7/2 and 4f5/2 orbitals, respectively. The oxygen (O) 1 s orbital peak is seen around ~ 530.63 eV and 532.22 eV in Fig. 2e. The valency is confirmed by the binding energy position of Ta 4f7/245,46,47,48. Therefore, the XPS results clearly indicate the stochiometric nature of Ta2O546,49,50. The similar results of XPS were obtained on thicker films which also confirms the similar stoichiometry surfaces of both the films, but this technique has a limitation and only films up to ~ 2 nm can be probed below the surface.

(a–c) XPS results of ITO thin films, (a) indium (In) peaks related to 3d3/2 and 3d5/2 orbitals, (b) Tin (Sn) peaks related to 3d3/2 and 3d5/2 orbitals, (c) Oxygen (O) peak related to 1 s orbitals. (d,e) XPS results of Ta2O5 thin films, (d) tantalum (Ta) peaks related to 4f7/2 and 4f5/2, (e) Oxygen (O) peak related to 1 s orbitals.

The morphologies of these films were confirmed using field-emission-scanning-electron-microscope (FESEM) and the results are shown in Figs. 3a–d and 4a–f for two distinct thicknesses and top electrodes respectively. The top surfaces of these films clearly show a distinct morphology for two different thicknesses regime. The thinner films show smaller grain size of ~ 15–20 nm and thicker films show a larger grain size ~ 100–150 nm mentioned in Fig. 3b, which seems to be grown larger out of these smaller grains (visible from the fine structures), as the films gets thicker as also suggested by the root-mean-square (RMS) roughness value of these films ~ 1.5 nm is also found to be independent of the thickness. The similar topographic surface was also observed with top electrode layer that confirms layer-by-layer smooth growth. Also, no major defects such as macroparticles and pinholes are seen on the surface of devices. These devices were also observed under optical microscope and scanning electron microscope before to rule out any major deformity on the sample surface (as shown in Fig. S2).

(a,b) FESEM topographic images of thinner and thicker films grown on ITO coated substrates (c,d) their approximate distribution of particle size.

(a–c) FESEM topographic images of Al/Ta2O5/ITO and (d–f) ITO/Ta2O5/ITO at different magnifications.

The current–voltage (I–V) characteristics of asymmetric (Al/Ta2O5/ITO) and symmetric (ITO/Ta2O5/ITO) RS devices are measured in current-perpendicular-to-plane geometry by changing the bias voltage from 0 V → -10 V → 0 V →  + 10 V → 0 V → -10 V → 0 V in a triangular sweep. The bottom contact on ITO was grounded and the top contact is connected to on the top electrode while taking the measurements. Repeated datasets were taken at different locations to check the overall statistical behavior of the device. Figure 5a–f shows the analysis of 50 continuous cycles of I–V curves (plotted on log Y-axis) for three Ta2O5 film thickness of ~ 20, ~ 80 nm and ~ 270 nm of asymmetric and symmetric RS devices, respectively. The IV cycles show a clear hysteresis during the triangular sweep, indicating a nonvolatile bipolar resistive switching behavior. In these graphs, the high-resistive-state (HRS) and the low-resistive-states (LRS) are depicted by the black and red lines for the negative bias polarity, and the blue and green lines for positive bias polarity. After 50 cycles, there is no major change in the shape of I–V curves and the overall RS characteristic is retained, except the hysteresis get slightly narrower, which is expected in a typical memristive type behavior. Interesting, the overall shape of RS curves changes of asymmetric device as the film goes through a transition from thinner to thicker regime, as seen in Fig. 5a–f and Figs. S4 and S5. First, the minima in the currents are not centered around zero bias but observed around ± 0.2 V. Similar “butterfly shape” or ‘battery-like characteristics” of IV curves have been observed by many other groups in different materials such as Pt/MoOx/ITO51, other metal-oxides earlier due to internal built-in potential and non-Faradaic capacitive (NFC) capacitive effects29. Clearly, as the film thickness goes through a transition, the battery like characteristics are well defined and the overall operating current and voltages are significantly reduced, giving the operating power in the range of ~ 20–100 nW depending on the nature of top metal electrode, which is lower compared to other recent studies14,30,35. Thickest films (Fig. 5c,f) on the other hand become unstable and showed a random behavior for both electrodes.

Resistive switching characteristics of asymmetric and symmetric devices with three distinct thicknesses of Ta2O5 film (~ 20 nm, ~ 80 nm, ~ 270 nm). Continuous 50 current–voltage (I–V) sweeps, highlighted 1st sweep.

Although the hysteresis is weak at one of the voltage polarities (positive for Al and negative for ITO), but an opposite polarity is always needed to completely reset the device. The preferential polarity could be due to the work function mismatch between the Al and ITO (Fig. S3). Also, the current range is also dependent on nature top electrode and the voltage polarity. These results can be explained using the band-diagram shown in Fig. 6a–d. The band diagram shows the respective positions of the Fermi levels, conduction band, and valence band of the top layers (Al, ITO), the intermediate layer Ta2O5, and the bottom layer ITO. In an asymmetric device (Fig. 6a), the Fermi level of the top electrode (Al) lies below the conduction band position of Ta2O5, but the Fermi level of ITO (degenerate semiconductor) is almost at the same level as the conduction band position of Ta2O5. So, under zero bias conditions (Fig. 6a), the electrons are expected to flow from Ta2O5 to Al but not from Ta2O5 to ITO, leading to a charge depletion at the Ta2O5/Al interface (band-bending). Therefore, a higher voltage is needed to overcome this barrier for tunneling (at higher bias) from Al to Ta2O5 as represented in Fig. 6b under biased condition. This observation is consistent with battery-like characteristics, as this barrier can contribute to an additional NFC. On the other hand, in a symmetric device (Fig. 6c,d), such a barrier is not formed at the interface, resulting higher current being observed at low bias voltages. In the case of the thickest film, this barrier does not play a significant role in overall direct or Fowler–Nordheim tunneling. Instead, the current is primarily dominated by bulk transport through Ta2O5 layer, which is heavily influenced by film defects. Consequently, no consistent Resistance Switching (RS) behavior has been observed. It is important to note that the IV characteristics for both thinner and thicker films are similar, except for large jumps and fluctuations in the hysteresis. Even the battery like characteristics could be observed. These large jumps and hysteresis could be attributed to bulk transport dominated by the conduction of through defects, in contrast to the tunneling mechanism observed for thinner and intermediate thicker films. The higher current observed in Fig. 5b,e can be attributed to the high degenerate nature of ITO and its respective Fermi level position with respect to the Ta2O5 band position. It should be noted that even in the asymmetric device, the higher current for the positive electrode is always observed, where the electrons transport from the bottom ITO to Ta2O5. This explains the higher asymmetricity in current (towards the positive bias) in asymmetric devices.

The schematic of energy band-diagram of (a,b) asymmetric device under zero-bias and biased conditions and (c,d) symmetric device under zero-bias and biased conditions.

Their endurance and retention of these devices are shown in Figs. 7 and 8 respectively. It has been observed that the films showing the battery-like characteristics relatively showed enhanced endurance and retention (Figs. 7b, 8b) compared to other films (Figs. 7a,c, 8a,c), as also reflected from the lower values of σ/μ extracted from the cumulative probability graphs shown in Fig. S6. Interestingly, thinner films showed better endurance and retention properties with ITO electrode.

Endurance property of asymmetric and symmetric devices with three distinct thicknesses of Ta2O5 film (~ 20 nm, ~ 80 nm, ~ 270 nm) of continuous 50 cycles.

Retention property of asymmetric and symmetric devices with two distinct thicknesses of Ta2O5 film (~ 20 nm, ~ 80 nm, ~ 270 nm) of 103 cycles.

To gain the understanding of the mechanism, these curves were linear fitted with different conduction mechanisms as per the procedure mentioned elsewhere13. The I–V curves in Fig. 5 could be the linear fitted with ln (I) vs. ln (V) as shown in Fig. 9, giving the slope values between ~ 1 and 2 that confirms the direct tunneling or defects assisted tunneling [space-charge-limited-conduction (SCLC)] is the dominant conduction mechanism. The direct tunneling from bottom to top electrode is not feasible for such a larger thickness. Therefore, the formation of filamentary path can also be concurrent mechanism with the trap-assisted tunneling. The weak asymmetricity in I–V curves is caused by the asymmetric nature of tunneling barrier due to the different work functions of electrode and insulator13,52,53,54,55. Compared to ITO as a top electrode, the Al and Ni coated metal tips (Supplementary Fig. S5) showed the battery-like characteristic, which is expected as these metals are more likely to participate in the redox reactions and change the local surface chemistry due higher oxygen affinity56 during the filament formation. On the other hand, thinner films do not have enough capacitance to hold the charge and the leakage current can kill the battery-like characteristics.

Linear fits between ln (I) vs ln (V) of resistive switching characteristics of asymmetric and symmetric devices for three distinct thicknesses of Ta2O5 (~ 20 nm, ~ 80 nm, ~ 270 nm).

To further probe these effects, these films were also measured by increasing the range of applied voltage and the compliance current to see the role of Joule heating17. The overall I–V characteristic and ZBC is shifted upwards every time the range of sweeping voltage is increased, representing the multiple intermediate-resistive-states (IRS), as shown in Fig. 10a–c. Similar behavior could also be seen when the range of sweeping voltage is fixed, and the external temperature is increased (as shown in the Supplementary Fig. S7), which further confirms Joule heating through voltage/current pulses17. Interestingly, each IRS states can still be tuned between LRS and HRS states. We explain the mechanism through the help of a schematic diagram shown in Fig. 10d, based on the in-situ transmission electron microscopy imaging by other groups57. It is illustrated that different IRS states can be stabilized due to formation of different filaments having specific lengths and widths, depending on the range of operation voltage and compliance current. The voltage sweep causes the oxygen vacancies to migrate and forms the metallic filaments of Ta, TaO and TaO2 phases34,57. However, the LRS and HRS can still be tuned around each IRS through controlling the tunneling current by modulation in the filament lengths. It is important to note in Fig. 10c, each time the range of operation voltage and compliance current is increased, the battery-like characteristics gets weaker which could be due to fact that the formation of larger metallic filaments within the insulating matrix57 can effectively decrease the NFC, and hence weaken the total internal field.

(a,b) I–V curves with increasing operating voltage and compliance current (c) the zoomed graphs showing the two current minima (in thicker films) getting closer, after increasing the range operation voltage and compliance current. (d) The schematic diagram explaining multiple intermediate-resistive-states (IRS) states and the low/high resistive states (LRS/HRS) tuned around each IRS through the modulation of filaments.

In conclusion, we have used the tantalum oxide thickness, top electrode material and Joule heating through voltage and compliance current as controlling parameter to tune the overall RS characteristics in a highly transparent a-Ta2O5 and a-ITO thin films. Two distinct a-Ta2O5 thicknesses give completely different shapes of I–V characteristics. Thinner films showed a conventional RS behavior, while thicker films showed a battery-like characteristic. The RS of the device is explained by the filamentary type of mechanism where the low and high resistive states can be tuned through the modulations in filaments lengths and width. In thicker films, compared to ITO as electrode the pure metals showed the battery-like characteristic due to higher oxygen affinity for redox reactions and Faradaic capacitive effects. This study also opens new opportunities for understanding the battery-like characteristics in thicker films and incorporation of nanobattery concepts in tantalum oxide based memristors and RS devices.

All data generated or analysed during this study are included in this published article and its supplementary information files.

Ohta, H. & Hosono, H. Transparent oxide optoelectronics. Mater. Today 7, 42–51 (2004).

Article CAS Google Scholar

Kim, C. C., Lee, H. H., Oh, K. H. & Sun, J. Y. Highly stretchable, transparent ionic touch panel. Science (80-. ). 353, 682–687 (2016).

Bhatnagar, P. et al. Transparent photovoltaic memory for neuromorphic device. Nanoscale 13, 5243–5250 (2021).

Article CAS PubMed Google Scholar

Yang, Y. et al. Transparent lithium-ion batteries. Proc. Natl. Acad. Sci. U. S. A. 108, 13013–13018 (2011).

Article ADS CAS PubMed PubMed Central Google Scholar

Morales-Masis, M., De Wolf, S., Woods-Robinson, R., Ager, J. W. & Ballif, C. Transparent electrodes for efficient optoelectronics. Adv. Electron. Mater. 3, 1600529 (2017).

Article Google Scholar

Zheng, Z. et al. A fully transparent and flexible ultraviolet-visible photodetector based on controlled electrospun ZnO-CdO heterojunction nanofiber arrays. Adv. Funct. Mater. 25, 5885–5894 (2015).

Article CAS Google Scholar

Lee, H. E. et al. Skin-like oxide thin-film transistors for transparent displays. Adv. Funct. Mater. 26, 6170–6178 (2016).

Article CAS Google Scholar

Shang, J. et al. Thermally stable transparent resistive random access memory based on all-oxide heterostructures. Adv. Funct. Mater. 24, 2171–2179 (2014).

Article CAS Google Scholar

Singh, R. et al. Highly transparent solid-state artificial synapse based on oxide memristor. Appl. Surf. Sci. 536, 147738 (2021).

Article CAS Google Scholar

Gopinadhan, K. et al. Effect of Nb and Ta substitution on donor electron transport and ultrafast carrier dynamics in anatase TiO2 thin films. J. Mater. Chem. C 3, 6329–6333 (2015).

Article CAS Google Scholar

Chang, T.-C., Chang, K.-C., Tsai, T.-M., Chu, T.-J. & Sze, S. M. Resistance random access memory. Mater. Today 19, 254–264 (2016).

Article CAS Google Scholar

Waser, R., Dittmann, R., Staikov, C. & Szot, K. Redox-based resistive switching memories nanoionic mechanisms, prospects, and challenges. Adv. Mater. 21, 2632–2663 (2009).

Article CAS PubMed Google Scholar

Rana, A. et al. Scaling behavior of resistive switching in epitaxial bismuth ferrite heterostructures. Adv. Funct. Mater. 24, 3962 (2014).

Article CAS Google Scholar

Yang, B. et al. A forming-free ReRAM cell with low operating voltage. IEICE Electron. Express 17, 1–4 (2020).

Article Google Scholar

Linn, E., Rosezin, R., Kügeler, C. & Waser, R. Complementary resistive switches for passive nanocrossbar memories. Nat. Mater. 9, 403–406 (2010).

Article ADS CAS PubMed Google Scholar

Yoon, J. H. et al. Pt/Ta2O5/HfO2-x/Ti resistive switching memory competing with multilevel NAND flash. Adv. Mater. 27, 3811–3816 (2015).

Article CAS PubMed Google Scholar

Rana, A., Li, C., Koster, G. & Hilgenkamp, H. Resistive switching studies in VO2 thin films. Sci. Rep. 10, 3293 (2020).

Article ADS CAS PubMed PubMed Central Google Scholar

Gao, X., Rosário, C. M. M. & Hilgenkamp, H. Multi-level operation in VO2-based resistive switching devices. AIP Adv. 12, 015218 (2022).

Article ADS CAS Google Scholar

Balatti, S., Larentis, S., Gilmer, D. C. & Ielmini, D. Multiple memory states in resistive switching devices through controlled size and orientation of the conductive filament. Adv. Mater. 25, 1474–1478 (2013).

Article CAS PubMed Google Scholar

Kumar, S., Agarwal, A. & Mukherjee, S. Electrical performance of large-area Y2O3 memristive crossbar array with ultralow C2C variability. IEEE Trans. Electron Devices 69, 3660–3666 (2022).

Article ADS CAS Google Scholar

Abbas, Y. et al. Compliance-free, digital SET and analog RESET synaptic characteristics of sub-tantalum oxide based neuromorphic device. Sci. Rep. 8, 1228 (2018).

Article ADS PubMed PubMed Central Google Scholar

Kumar, S. et al. Y2O3-based crossbar array for analog and neuromorphic computation. IEEE Trans. Electron Devices 70, 473–477 (2023).

Article ADS CAS Google Scholar

Jo, S. H. et al. Nanoscale memristor device as synapse in neuromorphic systems. Nano Lett. 10, 1297–1301 (2010).

Article ADS CAS PubMed Google Scholar

Pickett, M. D., Medeiros-Ribeiro, G. & Williams, R. S. A scalable neuristor built with Mott memristors. Nat. Mater. 12, 114–117 (2012).

Article ADS PubMed Google Scholar

del Valle, J., Salev, P., Kalcheim, Y. & Schuller, I. K. A caloritronics-based Mott neuristor. Sci. Rep. 10, 4292 (2020).

Article ADS PubMed PubMed Central Google Scholar

Venkatesan, T. & Williams, S. Brain inspired electronics. Appl. Phys. Rev. 9, 10401 (2022).

Article CAS Google Scholar

Lee, T. S. & Choi, C. Improved analog switching characteristics of Ta2O5-based memristor using indium tin oxide buffer layer for neuromorphic computing. Nanotechnology 33, 245202 (2022).

Article ADS Google Scholar

Valov, I. et al. Nanobatteries in redox-based resistive switches require extension of memristor theory. Nat. Commun. 4, 1771–1779 (2013).

Article ADS CAS PubMed Google Scholar

Zhou, G. et al. Capacitive effect: An original of the resistive switching memory. Nano Energy 68, 104386 (2020).

Article CAS Google Scholar

Guo, X. et al. SiO2/Ta2O5 heterojunction ECM memristors: Physical nature of their low voltage operation with high stability and uniformity. Nanoscale 12, 4320–4327 (2020).

Article CAS PubMed Google Scholar

Kim, B. Y. et al. Low power switching of Si-doped Ta2O5 resistive random access memory for high density memory application. Jpn. J. Appl. Phys. 55, 04EE09 (2016).

Kwon, S. et al. Structurally engineered nanoporous Ta2O5-x selector-less memristor for high uniformity and low power consumption. ACS Appl. Mater. Interfaces 9, 34015–34023 (2017).

Article CAS PubMed Google Scholar

Ji-cheng, Z., Di-tian, L. U. O., You-zhen, L. I. & Zheng, L. I. U. Effect of sputtering pressure and rapid thermal annealing on optical properties of Ta 2 O 5 thin films. Trans. Nonferrous Met. Soc. China 19, 359–363 (2008).

Google Scholar

Andrade, J. M. M., Rosário, C. M. M., Menzel, S., Waser, R. & Sobolev, N. A. Application of the quantum-point-contact formalism to model the filamentary conduction in Ta 2 O 5-based resistive switching devices. Phys. Rev. Appl. 17, 034062 (2022).

Article ADS CAS Google Scholar

Kumar, A., Krishnaiah, M., Mishra, D. & Hun Jin, S. Thickness dependent resistive switching behaviors in Ta2O5 layer at low temperature: Towards flexible, invisible, cryo-electronic applications in aerospace. Mater. Lett. 319, 132272 (2022).

Article CAS Google Scholar

Kim, S. et al. Engineering synaptic characteristics of TaOx/HfO2 bi-layered resistive switching device. Nanotechnology 29, 415204 (2018).

Article ADS PubMed Google Scholar

Chen, X., Bai, R. & Huang, M. Optical properties of amorphous Ta2O5 thin films deposited by RF magnetron sputtering. Opt. Mater. (Amst). 97, 109404 (2019).

Senthilkumar, V., Vickraman, P., Jayachandran, M. & Sanjeeviraja, C. Structural and optical properties of indium tin oxide (ITO) thin films with different compositions prepared by electron beam evaporation. Vacuum 84, 864–869 (2010).

Article ADS CAS Google Scholar

Amato, A. et al. Observation of a correlation between internal friction and urbach energy in amorphous oxides thin films. Sci. Rep. 10, 1670 (2020).

Article ADS CAS PubMed PubMed Central Google Scholar

Franke, E. et al. Dielectric function of amorphous tantalum oxide from the far infrared to the deep ultraviolet spectral region measured by spectroscopic ellipsometry. J. Appl. Phys. 88, 5166–5174 (2000).

Article ADS CAS Google Scholar

Lertvanithphol, T. et al. Spectroscopic study on amorphous tantalum oxynitride thin films prepared by reactive gas-timing RF magnetron sputtering. Appl. Surf. Sci. 492, 99–107 (2019).

Article ADS CAS Google Scholar

Dhaka, R. S. et al. An ultrahigh vacuum compatible sample holder for studying complex metal surfaces. Rev. Sci. Instrum. 81, 043907 (2010).

Article ADS CAS PubMed Google Scholar

Harinath Babu, S., Madhusudhana Rao, N., Kaleemulla, S., Amarendra, G. & Krishnamoorthi, C. Room-temperature ferromagnetic and photoluminescence properties of indium-tin-oxide nanoparticles synthesized by solid-state reaction. Bull. Mater. Sci. 40, 17–23 (2017).

Majumdar, H. S., Majumdar, S., Tobjörk, D. & Österbacka, R. Ferromagnetism in indium tin-oxide (ITO) electrodes at room temperature. Synth. Met. 160, 303–306 (2010).

Article CAS Google Scholar

Lawniczak-Jablonska, K., Wolska, A., Kuzmiuk, P., Rejmak, P. & Kosiel, K. Local atomic order of the amorphous TaO: X thin films in relation to their chemical resistivity. RSC Adv. 9, 35727–35734 (2019).

Article ADS CAS PubMed PubMed Central Google Scholar

Chen, Y. et al. Electroforming-free, flexible, and reliable resistive random-access memory based on an ultrathin TaO x film. ACS Appl. Mater. Interfaces 12, 10681–10688 (2020).

Article CAS PubMed Google Scholar

Kuo, Y. Reactive ion etching of sputter deposited tantalum oxide and its etch selectivity to tantalum. J. Electrochem. Soc. 139, 579–583 (1992).

Article ADS CAS Google Scholar

Simpson, R., White, R. G., Watts, J. F. & Baker, M. A. XPS investigation of monatomic and cluster argon ion sputtering of tantalum pentoxide. Appl. Surf. Sci. 405, 79–87 (2017).

Article ADS CAS Google Scholar

Skaja, K. et al. Reduction of the forming voltage through tailored oxygen non-stoichiometry in tantalum oxide ReRAM devices. Sci. Rep. 8, 10861 (2018).

Article ADS PubMed PubMed Central Google Scholar

Atanassova, E. Thin RF sputtered and thermal Ta2O5 on Si for high density DRAM application. Microelectron. Reliab. 39, 1185–1217 (1999).

Article Google Scholar

Wang, G. et al. Reversible voltage dependent transition of abnormal and normal bipolar resistive switching. Sci. Rep. 6, 36953 (2016).

Article ADS CAS PubMed PubMed Central Google Scholar

Thakare, V. et al. High sensitivity low field magnetically gated resistive switching in CoFe 2 O 4 /La 0.66 Sr 0.34 MnO 3 heterostructure. Appl. Phys. Lett. 100, 172412 (2012).

Zhang, Q., Rana, A., Liu, X. & Valanoor, N. Electrode dependence of local electrical properties of chemical-solution-deposition-derived BiFeO3 Thin Films. ACS Appl. Electron. Mater. 1, 154–162 (2019).

Article Google Scholar

Sawa, A. Resistive switching in transition metal oxides. Mater. Today 11, 28–36 (2008).

Article CAS Google Scholar

Maksymovych, P. et al. Polarization control of electron tunneling into ferroelectric surfaces. Science (80-. ). 324, 1421–1425 (2009).

Dhanaraju, L., Sangani, V. & Krishna, M. G. Oxygen affinity of metal electrodes as control parameter in tuning the performance of Cu x O-based resistive random access memory devices. Phys. Status Solidi A 216, 1900392 (2019).

Article Google Scholar

Park, G. S. et al. In situ observation of filamentary conducting channels in an asymmetric Ta 2 O 5–x/TaO 2–x bilayer structure. Nat. Commun. 4, 2382 (2013).

Article ADS PubMed Google Scholar

Download references

D. Khone acknowledges the research fellowship by BML Munjal University. A.S. Rana would like to acknowledge the SERB Core Research Grant (CRG/2021/001136) to support this work.

Centre for Advanced Materials and Devices, School of Engineering and Technology, BML Munjal University, Gurgaon, 122413, India

Darshika Khone & Abhimanyu Singh Rana

Department of Physics, Indian Institute of Technology Delhi, New Delhi, 110016, India

Sandeep Kumar & Sunil Kumar

UGC-DAE Consortium for Scientific Research, Indore, 452001, India

Mohammad Balal & Sudipta Roy Barman

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

A.S.R. and D.S.K. conceived the idea and executed overall experimental design, results analysis and wrote the original draft of manuscript. S.K. and S.K. performed ellipsometry, interpretation of spectroscopic data, and contributed to writing and revising the manuscript. M.B. and S.R.B. performed XPS measurements, interpretation, and analysis of data, and contributed to writing and revising the manuscript. A.S.R. supervised the overall work and reviewed the final manuscript.

Correspondence to Abhimanyu Singh Rana.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Khone, D., Kumar, S., Balal, M. et al. Resistive switching and battery-like characteristics in highly transparent Ta2O5/ITO thin-films. Sci Rep 13, 14297 (2023). https://doi.org/10.1038/s41598-023-40891-2

Download citation

Received: 03 May 2023

Accepted: 17 August 2023

Published: 31 August 2023

DOI: https://doi.org/10.1038/s41598-023-40891-2

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.